Our project's final aim was to create PHBV efficiently from waste or industrial by-products. Additionally, We wanted to reduce the need for downstream processing which is costly environmentally (see our LCA). To demonstrate this we used our bktb/phaCB operon grown on whisky pot ale to create plastic.</p>
 
&nbsp;&nbsp;
 
&nbsp;&nbsp;
 
&nbsp;&nbsp;
 
&nbsp;&nbsp;
Line 46: Line 47:
  
  
−
<p style="text-align:center;">Our project's final aim was to create PHBV efficiently from waste or industrial by-products. Additionally, We wanted to reduce the need for downstream processing which is costly environmentally (see our LCA). To demonstrate this we used our bktb/phaCB operon grown on whisky pot ale to create plastic.</p>
+
 
  
  

Revision as of 18:11, 17 October 2018

PhagED: a molecular toolkit to re-sensitise ESKAPE pathogens

 

 

 

 

 

Demonstrate

Our project's final aim was to create PHBV efficiently from waste or industrial by-products. Additionally, We wanted to reduce the need for downstream processing which is costly environmentally (see our LCA). To demonstrate this we used our bktb/phaCB operon grown on whisky pot ale to create plastic.

        

Secreation

Enter some text here and link parts!!



Figure 1. Six 50 mL cultures of phaCB/Bktb in M9 media and 1% glucose were set up with three containing Pot ale and the other three containing water. Colonies were set up to shake at 37 oC overnight for 64 hours.



We were able to grow our E. coli on media containing M9 salts, 1% glucose, and pot ale. Our negative control contained water instead of pot ale. Our cells grew similar in both types of media but grew lower than our model predicted. However, the pot ale did not negatively affect growth.

Figure 2. OD600 of cells grown in M9 media and 1% glucose with and without pot ale. Cells grown in pot ale and without pot ale similar growth curves.



Next we wanted to show that our cells could produce plastic growing in pot ale. Cells were grown for 64 hours and then had their dry cell weight measured before extraction (Figure 3).

Figure 3. Dry cell weight vs mass of plastic extracted of phaCB-Bktb cells grown in M9 media and 1% glucose with and without pot ale.



Figure 4. Melting temperature ranges of extracted plastic. Cultures grown on pot ale have consistant melting temperature ranges.